MD10

Masonry mortar 25kg

MD 10 is used for the construction of masonry from conventional clay bricks, cement bricks, and decorative bricks of any size and type. It can also be used in various small repair jobs. Homogeneous, ready-to-mix, industrial product of consistently high quality. It ensures good workability, increased application speed, it is economical and provides excellent results.

Σύσταση & Χαρακτηριστικά

• Mixture of high specifications grey cement, crushed marble of selected granulometry enriched with special improving additives. • It complies with the specifications: EN 998-2:2010, M2,5, W2. Granule size <2.4 mm.

Εφαρμογή

• The substrate must be clean and firm and it is recommended that it is wetted before application. • The contents of a bag shall be mixed with clean water (approximately 5.5-6.0 l/bag) using an electric mixer at low speed or a traditional mixer until a homogeneous mixture is obtained. The mixture remains workable for 3 to 4 hours (depending on the ambient temperature). Periodic stirring without adding additional water is required. The mixture is applied with a simple or serrated trowel. • The application of the paste and the installation of the building elements in their final position should be completed within a maximum of 10-12 minutes. • The final surface should be protected from rapid water loss and extreme weather conditions. If necessary, the surface should be wetted with clean water. • At the application stage, the temperature should be between +5 oC and +35 oC.

Συσκευασία & Φύλαξη

• In bags of 25 kg, on pallets. • In a dry place where frost does not form, for 12 months from the date of production, in unopened bags.

Κατανάλωση

Approximately 13-15 kg/m2, depending on the size of the bricks.

Τεχνικά Χαρακτηριστικά

Specifications: EN 998-2:2010, Μ10, W2, granule size<2.4mm

Granule size 0.0-2.4mm Consumption 13.0-15.0 kg/m2
Dry mortar density 1600 kg/m3 Resistance to compression 4.0 N/mm22
Capillary water absorption (Cm) 0.06 kg/m2. min0.5
Resistance to bending 1.4 N/mm22